RG type (Corrosion Resistant Tungsten Carbide)

Alloys featuring in that binder phase reinforcement is added so that the Co phase,which may cause corrosion,is solid-solution reinforced,thus improved in heat resistance corrosion ularly,electrolytic corrosion due to wire cut and corrosion after polishing are prevented. Reinforced binder phase reduces occurrence of chipping and thermal cracks.

Material grade	Density g/cm3	Hardness HRA	T.R.S. MPa	Comp.S. MPa	Application
RG1	15.0	92.5	2,450	6,080	Wire Drawing Die, Nozzle, Cutting Tool, Gause, Powder Molding, Drawing Tool for Light Impact, Guide, etc.
RG2	14.6	91.5	3,240	5,250	Powder Molding, Wire Drawing Die, Plug, Drawing Tool, Punching Tool, Roll Center, Mining Bit, Nozzle, Blade, Stone Tool, Ring, Gause, Cutting Tool, Guide Bush, Core, etc.
RG3	14.6	91.0	3,160	4,850
RG4	14.4	90.0	3,140	4,480	Drawing Tool, Punching Tool, Punch, Cutting Tool, Cutter, Ring, Plug, Powder Molding for Special Configuration, Upper/Lower Punch, Core, etc.
RG5	14.1	88.3	3,140	4,100

RGタイプ 耐蝕性合金

結合相強化剤を添加し、腐食の原因となるCo相を固溶強化することにより、耐熱、耐蝕性を向上させた合金。特にワイヤーカットによる電蝕や研磨後の腐蝕を防止します。また結合相を強化したことにより、チッピング、熱クラックの発生が減少します。

材質	JIS?CIS 記号	密度 g/cm3	硬度 HRA	抗折力 MPa	圧縮強度 MPa	用 途
RG1	VM20	15.0	92.5	2,450	6,080	伸線ダイス?ノズル?刃物?ゲージ?粉末成形型?軽荷重の絞り型?ガイド?他
RG2	VM30	14.6	91.5	3,240	5,250	粉末成形型?伸線ダイス?プラグ?絞り型?抜き型?ロール?センター?鉱山用ビット?ノズル?ブレード?石工具?リング?ゲージ?刃物?ガイドブッシュ?コアー?他
RG3	VM30	14.6	91.0	3,160	4,850
RG4	VM40	14.4	90.0	3,140	4,480	絞り型?抜き型?パンチ類?刃物?カッターナイフ?リング?プラグ?異形用粉末成形型?上下パンチ?コアー?他
RG5	VM50	14.1	88.3	3,140	4,100